Class x 2 EMI/RFI
Unit of Measure
Specifications
|
Dimensions
|
Alternating Current (AC) Voltage
|
Insulation Resistance at 20 Degree Celsius (ºC) (<70 % Relative Humidity (RH)) for 1 Minute (min) at 100 Volt (V) Direct Current Voltage (VDC) Applied
|
Dielectric Strength
|
Life Expectancy
|
Humidity Test
|
Features
|
Applications
Specifications
Available |
N/A {0} |
Manufacturer Stock |
N/A {0} |
Brands |
N/A Cornell Dubilier |
Manufacturer |
N/A Cornell Dubilier |
Capacitance |
N/A 1 µF |
dv/dt Rating |
N/A 400 V/µs |
Operating Temperature Range |
N/A -40 to +110 ºC |
Capacitance Tolerance (±) at 1 Kilohertz (kHz) Frequency, 20 Degree Celsius (ºC) Temperature |
N/A 10 % |
Frequency Range |
N/A 50 Hz60 Hz |
Maximum Dissipation Factor (Tan δ) at 1 Kilohertz (kHz) Frequency and 20 Degree Celsius (ºC) Temperature |
N/A 1 % |
Self-Inductance |
N/A ≤ 1 Nano-Henry per mm of lead spacing |
Impulse Voltage (24 Pulses) |
N/A
C < 1 uF Vp= 2.5 kVDC C > 1 uF Vp= 2.5 kV√C |
Capacitance Temperature Coefficient |
N/A ±100 ppm/ºC-200 ppm/ºC |
Construction |
N/A Metallized Polypropylene film |
Electrodes |
N/A Vacuum deposited Metal layers |
Coating |
N/A Flame retardant Solvent resistant plastic case with epoxy end fill (UL94V-0) |
Lead Terminations |
N/A Tinned Copper Clad Steel Leads |
Dimensions
Dimension L |
N/A 18 mm |
Dimension H |
N/A 18.5 mm |
Dimension T |
N/A 11 mm |
Dimension S |
N/A 15 mm |
Dimension d |
N/A 0.8 mm |
Alternating Current (AC) Voltage
Alternating Current (AC) Voltage for Underwriters Laboratories (UL)/Canadian Standards Association (CSA)1 | N/A 250 V275 V310 V |
Alternating Current (AC) Voltage for European Norms Electrical Certification (ENEC)2 | N/A 250 V275 V310 V |
Alternating Current (AC) Voltage for China Quality Certification (CQC) |
N/A 310 V |
Insulation Resistance at 20 Degree Celsius (ºC) (<70 % Relative Humidity (RH)) for 1 Minute (min) at 100 Volt (V) Direct Current Voltage (VDC) Applied
Terminal to Case Insulation Resistance at 20 Degree Celsius (ºC) Temperature (<70 % Relative Humidity (RH)) for 1 Minute (min) at 100 Volts (V) Direct Current (DC) Voltage Applied |
N/A > 30000 MΩ |
Terminal to Case Insulation Resistance at 20 Degree Celsius (ºC) Temperature (<70 % Relative Humidity (RH)) for 1 Minute (min) at 500 Volts (V) Direct Current (DC) Voltage Applied |
N/A > 5000 MΩ |
Dielectric Strength
Terminal to Terminal Dielectric Strength |
N/A
1333 VDC (4.3 x 310) VDC applied for 60 seconds Cut-off current: 10 mAdc Current limiting resistance: 1 Ω/V |
Terminal to Case Dielectric Strength |
N/A 2050 VDC (50/60 Hz) applied between the terminals and case for 60 Seconds and 20 ºC |
Life Expectancy
Note for Life Expectancy |
N/A 1000 hours at 110 ºC at 125% of rated voltage with once every hour the voltage is increased to 1000 VAC for 0.1 seconds |
Capacitance Change (Life Expectancy) |
N/A ≤ 10 % of Initially Measured Value |
Dissipation Factor (Life Expectancy) |
N/A ≤ 0.8 % at 1 kHz |
Insulation Resistance (Life Expectancy) |
N/A ≥ 50 % of initially specified value (T-T) |
- 1 For T> +85 ºC , The voltage must be decreased by 1.25 % per ºC
- 2 For T> +85 ºC , The voltage (DC/AC) must be decreased by (1.5/2.25) % per ºC